Characteristics

Trimethylolpropane trimethacrylate is a typical trifunctional monomer, and its viscosity is higher than that of monofunctional and bifunctional monomers, but compared with multifunctional monomers, its viscosity is relatively low, and it has good solubility. This monomer provides high cure speed and high crosslink density, and can form a hard, scratch-resistant and brittle cured film with excellent solvent resistance. Its price is relatively low, although it is irritating to the skin, it is still the most commonly used multifunctional monomer. It is ideal for various coatings anaerobic adhesive and composite applications.

Preparation

synthesis of Trimethylolpropane trimethacrylate: 40.25g (0.3mol) of trimethylolpropane and 90.41g (1.05mol) of methacrylic acid were added to the reactor equipped with a reflux condenser, a water separator, a thermometer, a stirrer, and an air sampling device respectively to inhibit the polymerization. Agent 0.39g (prepared by hydroquinone: phenothiazine=2: 1 mass ratio), CZ zirconium-based solid acid catalyst 1.21g, with water agent 100ml (prepared by the volume ratio of toluene: cyclohexane=45: 55) ), be gradually warming up to 85 ± 5 ℃ while stirring, the flow velocity that keeps feeding air in the reactor is 7ml/min, at 90-100 ℃ temperature, reacted for 5 hours (when the water agent was brought out without reaction to generate water is the reaction end point), and the filter residue obtained by filtration of the reaction solution is a CZ zirconium-based solid acid catalyst (recovered and reused). Activated carbon 2g was added to the reaction mother liquor, the temperature was raised to 45±5°C with stirring, maintained for 15 minutes, filtered while hot, and the filtrate after the activated carbon was removed was evaporated under reduced pressure to obtain the target product trimethylolpropane trimethacrylate. 110g, the purity is 98.2%, the acid value is ≤0.5mg/g (the acid value detection method is determined according to the method of GB 1668-8), and the esterification rate is 98.2%.

Flammability and Explosibility

Nonflammable

General Description

Trimethylolpropane trimethacrylate is a carbonyl compound.